Beads are really dark after they cool
Hello,
I am fairly new on the glass bead work. I do have a good setup. Propane and Oxy. and I am using both a fiber blanket and a Kiln. I used to go down to my local bead shop and buy my glass from her. Time change and the store is gone. I never had any issues with the glass when I bought it from her. I am just making simple 2 or 3 color beads. I just bought Devardi Glass COE 90 5-6 mm rods. When I do any color mixing the beads go very dark. So when i use a very light blue or green after they cool they are so dark you cant really see the colors. What the heck am I doing wrong? I have never had this problem. Could it be the glass? Any advice would be great. Thank you ! |
What colors are you mixing?
The copper in greens doesn't play well with the sulfur colors (like yellow) for example, and if you use one on the other you get a dark line, so mixing might just make them turn dark I would think. |
All times are GMT -7. The time now is 10:41pm. |
Powered by vBulletin® Version 3.7.5
Copyright ©2000 - 2024, Jelsoft Enterprises Ltd.