Quote:
Originally Posted by Robin Passovoy
I've tried using iridescent glass before, the Bullseye fusible stuff, and didn't get very good results. It doesn't take direct flame very well, or the constant fluctuations in temperature that torchwork involves. You could try treating it like dichroic, laying it coated-side down so that the base glass provides a protective coating.
|
How would that work if you can't mix glass?