Quote:
Originally Posted by Elizabeth Beads
snip...
There's enough silver in 96 Raku, MC and MCD that they should all be fine on the surface of 104.
...snip
|
Um, huh? I don't mean to pick on you Liz, but that statement doesn't seem to make sense. It sounds like you're saying that more silver in a glass makes the compatibility better with glass of a very different COE. (Which is not the case.) Can you please clarify? I would let this slide, but there is so much misinformation floating around the lampworking community about glass compatibility that adding more to the pile isn't going to help.
Brad