I have toyed with the cadmium colors and stuff and I am getting better with working them without bubbling them. I have been assuming that the wrinkling was from too much heat. Or bad flame chemistry or something . As far as moving the glass after it has gotten too cool, I have thought that too, but I will get a piece up to really hot and try to let it cool slowly with no movement at all I feel like other than rolling and still have the same effect or if it is already there I can't work it out, no matter how hot it gets
|