I only use 104 and 96. If you are new (or if newbies are reading), please remember you can't mix coes. I started with 96 because I was fusing glass before I made beads, but now I like both for different things. 96 is slightly stiffer so is great for doing sculptural items. Both have amazing color selection. You can never have too much glass!