Quote:
Originally Posted by LyndaJ
unless you are mixing COE's like Reichenbach frits on 104 or 90. I have had NO success with compatability with a lower annealing cycle. Some beads too > 6 mo to crack.
I use 970 generally unless I'm using silver glass.
|
I could see where those might be problematic. I have some uroboros glass for use with my frits - I don't mix COEs any more.