Larry I have a creation station with wrist rests, but I make pendants, & must move the piece at different angles during the compression process, I work 14mm that is suspended on 9mm to reduce weight. It is necessary to spin the piece for quite a bit, melting everything in. Each pendant is at least 25 - 30 min to make, was thinking that more heat would maybe shorten the melting time, I am not interested in making anything bigger, just faster. Not sure what a yolk is? If it is something stationary, it would not help much as I focus the heat differently throughout the process of making a pendant holding the maria at different angles to achieve different effects.