Hi MJ!
Happy to see you posting
I anneal at 960 with the standard ramp down. I gave this a good work out last week just to test out using different clears and had no problems with cracking at all. I really love the diamond clear with brass frit because it just adds that extra sparkle.
Side note
I had pure copper chain that I bought at Micheals last week and gave it a try in a bead. It turned out pretty cool.
What do you anneal your silver glass at. I'm at 960 for that too. I have not noticed a difference but if they come out even sweeter with a lower temp I will give it a try.
Hugs, Dawn