Garaging is ideal - mostly because the glass is dealt with straight away.
Batch annealing's main risk is that the longer unannealed beads are left, the more time strain points have to play and run amok.
That's my take on it anyway. I don't run my big kiln every session because it's expensive when I only make a handful of beads at a time, and I don't generally do large beads.