Technically yes.
Provided that my math is correct..For a 1" thick piece of Moretti glass the maximum(fastest) slow cooling rate (annealing through strain) is 3.74 degrees F/min or 224 degreesF/hour.
So 100 DPH is acceptable as long as your largest piece in the kiln doesn't exceed a 1" thickness.