Sodium flare is present when working soft glass also..not as much of a hazard persay but it makes it impossible to see the bead/glass when it's in the flame and can cause eye irritation to light sensitive people if you work for several hours.
It's like night and day. Working glass of any kind without didymiums, (AUR-92/ACE lenses are ideal) is just no good.