Great idea... the only point I have issue with is Jim's suggestion that the beads don't need to be ramped down to strain point slowly. They do! They may not break, but they aren't "annealed" unless you do this. It's still glass and it needs to be cooled at a controlled rate to @ 950... don't want anybody to get started off with misinformation.