Just thought I'd pop in with a question for those who have had beads crack - what are you annealing at? If you are annealing at a lower temperature because you are also using silver glass in the bead or are making silver glass beads in the same sitting, that could also be a factor. Just something to consider. I haven't tried this yet, but I know I pretty much just use my lower temp longer annealing time schedule for almost everything anymore because I use silver glass so often, so that's what made me think of this.
Dawn - could you post your annealing schedule?