Quote:
Originally Posted by glassactcc
Well, not entirely but if there is a crack that is not visible yet under the bead, it should make it start to travel faster from what I have heard, but I don't know that to be 100% fact. Maybe someone else could chime in on that theory too
|
Being a physicist by education, I'll chime in. If there are cracks you can make them travel (faster) by changing temperature, especially if the cracks are due to a difference in COE. Putting them in the freezer should do at least something. - So should putting them in the oven, for that matter. -
__________________
Aloha, Maren - HiloBeads: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Palms Etc. tropical seeds and cuttings: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
HotHead on bulk propane and a Glasshive kiln
|