CIM Shocky?
Does anyone else find CIM to be more shocky than other 104's? I am having a heck of a time with Fiddlehead green. It keeps shattering and breaking off in chunks!
|
2014-08-01, 5:00am
|
|
Senior Member
|
|
Join Date: Jan 31, 2010
Location: London, UK
Posts: 358
|
|
Not in general, no, but specific rods of whatever colour and manufacturer can always be different! Try looking at the end and see if it has airholes running through it? Though I don't usually get that with CiM's rods at all.
Some colours or rods need putting back in the flame a bit more slowly, or they can shock off just above the part you'd previously heated. I get that with all manufacturers though.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. | To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. | To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. | To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. | To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-01, 5:02am
|
|
Senior Member
|
|
Join Date: Jun 20, 2005
Location: foothills east of Seattle
Posts: 2,739
|
|
You can't paint a whole brand of glass with one characteristic, so no - CiM as a whole is not any more shocky than any other brand of 104 coe glass.
As a tester for CiM glass, what I can tell you is that some of their opaques - greens more than any other in my experience, can be shocky. The darker, more saturated greens and teals have had some tendency to shock, but that's pretty much par for the course in many opaque greens across the brands, in my experience. The lighter opaques don't have any shocky issues that I can recall. Transparents haven't been shocky at all.
Once I had a rod of Mermaid shock like crazy, but the rest of the batch was fine!
I've had good luck preheating the ends of shocky rods of any brand in the kiln for a few minutes before using them. Or, I just introduce them to the flame really slowly.
I hope this helps!
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-01, 5:53am
|
|
hyperT
|
|
Join Date: Jan 31, 2013
Location: San Antonio, Texas
Posts: 582
|
|
Try adjusting your fire the glass may need more or less oxygen.
|
2014-08-01, 6:25am
|
|
Disconnected
|
|
Join Date: Jan 31, 2007
Location: Normandy, France
Posts: 1,323
|
|
My understanding is that all CIM colors are handpulled. That might be why you're finding them shockier (can we invent this word?)
My experience is different from Kandice's, I recently used Linen and Dried Sage, both pale greens, and they were nasty shocky. I even got burned twice by flying bits, which had not happened to me in a few years.
All in all, I don't find them more shocky, just as shocky as other brands. If we're going to talk about brands, Devardi beats them all.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-01, 7:35am
|
|
Senior Member
|
|
Join Date: Jun 22, 2005
Location: west of Atlanta, Georgia
Posts: 5,371
|
|
I was smacked in the lip and hand and arm yesterday by Effetere gray. Sometimes I think the rod got banged around more than anything. Or like when it gets dropped into the pvc pipe. I haven't found CIM any shockier actually. It's just a crap shoot.
|
2014-08-01, 7:49am
|
|
I like to melt things
|
|
Join Date: Jul 22, 2008
Location: British Columbia
Posts: 2,163
|
|
I agree with the others - CiM is not shockier than glass from other manufacturers. Most of the time for me with CiM, when I come across a really shocky rod, it has one or two friends in my stash but the rest of it is fine.
I did have one experience, though, where the entire pound of Khaki that I had bought was a self-fritting disaster, and when I told Kathy at CiM about it, she replaced it for me. She cares deeply about the quality of her product and our experience using it, so if your problem is really dire and seems to be throughout the rods that you bought, maybe let her know.
__________________
Melanie
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-01, 9:48am
|
|
Slogan Challenged...
|
|
Join Date: Mar 21, 2009
Location: Maricopa, Arizona
Posts: 6,287
|
|
I find all 104 greens to be a little suspect! Nile was the worst for me for a while, but I'm never sure how a new rod of almost any green will work out.
I don't have Fiddlehead, but I've been pleased with Iguana and Kermit. It seems the newer ones are not that bad. Except for Celadon.
Celadon is my current nightmare. I have not managed to even make one bead from this color yet. I pick the chunks up off my worktable and try to melt those and they shock as well. Horrible, and such a pretty color too. I don't have a way to preheat, so I'll really have to try again with a low flame when I have the time.
__________________
Kristin ~
Facebook: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Etsy: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-01, 10:14am
|
|
Senior Member
|
|
Join Date: Aug 31, 2006
Location: Knoxville, TN
Posts: 2,215
|
|
Wow. I have not had that experience with Celadon! My batch is very old though. It is a color I love.
__________________
Kathy
|
2014-08-01, 1:17pm
|
|
Senior Member
|
|
Join Date: Jun 11, 2005
Location: SUNNY FLORIDA~West Coast!
Posts: 9,423
|
|
I once had a batch of Canyon de Chey that was very unstable. Kathy didn't want to replace it so I had to sell it with a disclaimer on it.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Still North America's Largest Lauscha Dealer!
Now reopened in South Florida!!
Like US on Facebook ! To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-01, 3:16pm
|
|
Fugitive from the Dogstar
|
|
Join Date: Aug 01, 2013
Location: Southern California
Posts: 289
|
|
Quote:
Originally Posted by KJohn
I find all 104 greens to be a little suspect! Nile was the worst for me for a while, but I'm never sure how a new rod of almost any green will work out.
I don't have Fiddlehead, but I've been pleased with Iguana and Kermit. It seems the newer ones are not that bad. Except for Celadon.
Celadon is my current nightmare. I have not managed to even make one bead from this color yet. I pick the chunks up off my worktable and try to melt those and they shock as well. Horrible, and such a pretty color too. I don't have a way to preheat, so I'll really have to try again with a low flame when I have the time.
|
Great, I just ordered Celedon to try out. My last order of Dirty Martini is shockier than sh**! It freaked me out a bit so it went back into the drawer and I haven't touched it since.
|
2014-08-01, 5:47pm
|
|
Slogan Challenged...
|
|
Join Date: Mar 21, 2009
Location: Maricopa, Arizona
Posts: 6,287
|
|
So sorry Carol! Hope it works out better for you, I didn't try another rod of it so it might just be the one in the bundle that decided to act up. I was too freaked out as well, lol.
__________________
Kristin ~
Facebook: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Etsy: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-02, 7:49am
|
Jer. 29:11, Prov.10:19
|
|
Join Date: Jun 29, 2005
Posts: 487
|
|
Quote:
Originally Posted by KJohn
I find all 104 greens to be a little suspect! Nile was the worst for me for a while, but I'm never sure how a new rod of almost any green will work out.
I don't have Fiddlehead, but I've been pleased with Iguana and Kermit. It seems the newer ones are not that bad. Except for Celadon.
Celadon is my current nightmare. I have not managed to even make one bead from this color yet. I pick the chunks up off my worktable and try to melt those and they shock as well. Horrible, and such a pretty color too. I don't have a way to preheat, so I'll really have to try again with a low flame when I have the time.
|
I've had that problem with Celadon off and on--the latest batch is VERY shocky. I can use it by preheating the end in the kiln, but that's all I get, it pops off at the temperature line. Just hope the next batch is better.
|
2014-08-02, 8:09am
|
|
Senior Member
|
|
Join Date: Jun 11, 2005
Location: SUNNY FLORIDA~West Coast!
Posts: 9,423
|
|
Another way to deal with shocky glass is to heat it with just your propane flame first and then slowly add in your oxygen. Paula
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Still North America's Largest Lauscha Dealer!
Now reopened in South Florida!!
Like US on Facebook ! To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-02, 8:15am
|
|
one day at a time
|
|
Join Date: Jun 27, 2005
Location: We are MOVING!!!
Posts: 8,319
|
|
The worst one of all glass I've tried and it's even beats Effetre Anice, is Effetre Sage Green. Ihave better luck with the Avocado.
__________________
You live in a world of money. Money means choices. No money, no choices. Welcome to reality.
Melody (Marlee Matlin) from Switched at Birth
|
2014-08-11, 1:37am
|
|
Senior Member
|
|
Join Date: Jun 28, 2008
Location: South Australia, Australia
Posts: 492
|
|
I was going to start a new thread about this, but saw this one so I will add that I just got some of the new CIM heartthrob, and it should be called "heart shock"! I know how to deal with shocky glass, but this one was just awful. I ended up tossing the rod into the bin and am afraid to use any more of it.
VERY disappointed and feeling ripped. It's a nice red too, as I got some of it to make a bead, but it just popped all over the place. I have found CIM to be the one that is most shocky, in my experience. And there was a honey something or other by Effetre that shocked, but I could tame that.
I must get the bad boys
|
2014-08-11, 2:31am
|
|
Unmedicated since '62
|
|
Join Date: Jan 18, 2009
Location: Hunter Valley, Australia
Posts: 5,907
|
|
Gellys sty - frit on a stick!
__________________
Deb
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - my 17yo sons first novel
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - download, get organised, enjoy
|
2014-08-11, 2:34am
|
|
Unmedicated since '62
|
|
Join Date: Jan 18, 2009
Location: Hunter Valley, Australia
Posts: 5,907
|
|
The worst shocky glass ever is Anice! And the first time i ever picked up a rod of glass to make beads it was anice
__________________
Deb
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - my 17yo sons first novel
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - download, get organised, enjoy
|
2014-08-11, 7:33am
|
|
Senior Member
|
|
Join Date: Aug 31, 2006
Location: Knoxville, TN
Posts: 2,215
|
|
Sounds like the recent stock is shockier than old batches. The stuff I have had the worst problems with are the usual suspects from Effetre, and then the old Vetro odd lots. I have never worked up the nerve to try my Anice White!
Beadskadoo, Honey Crunch. I think that was Vetro? I love it though, so I baby it along.
I have some kind of dark blue transparent effetre special color that just chunks off in 1/4" perfectly fractured sections. I have not been able to do anything to it to make it better. It sucks a$$. Blue Ivory? Shoot, I can't really remember which one it was.
__________________
Kathy
|
2014-08-11, 4:06pm
|
|
Dancing in the Flame
|
|
Join Date: Jul 05, 2014
Location: Ottawa, ON
Posts: 71
|
|
I find CIM shocky - fiddlehead green specially. I find if I sit them on top of my kiln on the rod warmer they aren't as bad.
__________________
Lou
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-11, 9:29pm
|
|
I like to melt things
|
|
Join Date: Jul 22, 2008
Location: British Columbia
Posts: 2,163
|
|
I get the odd rod of shocky CiM, but it is rare to have that problem with CiM for more than a few rods in any given batch. The very worst shockiness problems I have had were with Effetre Anise White and Vetrofond Honey Crunch. Those colours are virtually unusable for people without saintly patience. Every single rod, fritplosion city.
By comparison, even the very shockiest CiM experience I have ever had (which was a whole pound of pretty unusable Khaki) was a total picnic.
__________________
Melanie
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. - To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-11, 11:54pm
|
|
rainbowchasingtimewaster
|
|
Join Date: Jun 10, 2005
Location: Willow Glen, CA
Posts: 4,457
|
|
Effetre dark pink. I actually just clean my work table before I use it and let it pop off into frit. I pick up the pieces, mash it up to get rid of any air bubbles, and pull it into thick stringers (or narrow rods, depending on how you look at it.). It's the only way I can get it to a usable form.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. Lori Peterson - Try telling a Dachshund no and you will understand the true meaning of futility.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. * To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. * To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. * To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. * To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. * To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. *f To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. * To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-12, 12:38am
|
|
Member
|
|
Join Date: Feb 07, 2014
Location: Beachmere, QLD Australia
Posts: 45
|
|
The same thing happened with Calico for me, Lori. When I'd gone through two thirds of the rod without making a single bead, I put all the chunks in a metal tray in the kiln. Then picked them up with the melted end of a rod. That rod was the ugliest thing I'd ever seen but I did get to make some spacers. Trouble is, I LOVE those spacers. Now am I prepared to buy more calico? I honestly don't know 😳
Caitie
|
2014-08-12, 1:50am
|
|
Senior Member
|
|
Join Date: Jun 20, 2005
Location: foothills east of Seattle
Posts: 2,739
|
|
Yep, Effetre Dark Pink, Opal Yellow (especially when it has holes) and Sage Green. Sometimes Copper Green, too. Seems Effetre can't handpull anything without catching a bunch of air holes. All of those are terribly shocky. Yikes!
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-13, 9:06am
|
Member
|
|
Join Date: Mar 25, 2013
Posts: 35
|
|
I've only been making beads for about a year but, one of the first things I was told is that CIM glass tends to shock easier. But, I never noticed a true difference between CIM and any other glass. I agree with the others in that it seems to be more by the individual color.
Any form of Goldstone tends to crumble for me, no matter what I do.
I've found that the easiest way to remedy a shocky color is to preheat the rod, if you can.
|
2014-08-14, 7:47am
|
|
Nerwbie Glass Junkie
|
|
Join Date: Oct 24, 2010
Location: Brisbane, Sunshine State, Australia
Posts: 2,133
|
|
I agree with the others, in general CIM is no worse than any of the other manufacturers for shockiness.
But Fiddlehead, OMG, it's definitely up there as frit on a stick! It's shocking (pun intended! ).
__________________
Toowoomba here I come ...
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-14, 8:43am
|
|
Fugitive from the Dogstar
|
|
Join Date: Aug 01, 2013
Location: Southern California
Posts: 289
|
|
Kristin - got my batch of Celedon, not that shocky thankfully!
|
2014-08-14, 8:43am
|
|
Fugitive from the Dogstar
|
|
Join Date: Aug 01, 2013
Location: Southern California
Posts: 289
|
|
Quote:
Originally Posted by kandice
Yep, Effetre Dark Pink, Opal Yellow (especially when it has holes) and Sage Green. Sometimes Copper Green, too. Seems Effetre can't handpull anything without catching a bunch of air holes. All of those are terribly shocky. Yikes!
|
Eff Mint Green is pretty wicked too.
|
2014-08-14, 9:08am
|
|
Slogan Challenged...
|
|
Join Date: Mar 21, 2009
Location: Maricopa, Arizona
Posts: 6,287
|
|
Quote:
Originally Posted by 1knitchick
Kristin - got my batch of Celedon, not that shocky thankfully!
|
Good! The rod I was using was a thick one, so maybe I'll get lucky with the rest
__________________
Kristin ~
Facebook: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Etsy: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-08-14, 9:31am
|
|
Senior Member
|
|
Join Date: Aug 31, 2006
Location: Knoxville, TN
Posts: 2,215
|
|
Quote:
Originally Posted by MrsD
I agree with the others, in general CIM is no worse than any of the other manufacturers for shockiness.
But Fiddlehead, OMG, it's definitely up there as frit on a stick! It's shocking (pun intended! ).
|
Looks like Fiddlehead was one of the greens I missed - sounds like a good thing! I am a pushover for any green.
__________________
Kathy
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -7. The time now is 11:43pm.
|