When to use the kiln???
First off, let me start by saying You guys ROcK!!!
I was told that when I make a bead that is "large-ish", it should be put in the kiln - what size is "large-ish" as a general rule. At what point do you put it in the kiln? After it has been cooled down and taken off the mandrel?
I have a Paragon XPress Kiln that can fire up to 2300degrees and is digital. What is my ramp up time, hold time, etc?
THANKS ALOT FOR ALL OF UR HELP!!!!
I LOVE LAMPWORKING!!
|
2007-12-30, 4:51pm
|
|
tinkmartin.etsy.com
|
|
Join Date: Jun 10, 2005
Location: Toledo, Ohio
Posts: 7,452
|
|
Hi dulceisler, and welcome!
All beads should be kiln-annealed at some point. How you handle that is the product of many variables. Ideally, in my opinion, your work should go into the kiln as soon as you've finished work on it and it's just cool enough that you won't get marks on it from it laying on the kiln floor. It is, of course, still on the mandrel at this point, as it's just cooled off enough that it isn't glowing.
If your kiln has a bead door, this is a simple matter: Make a bead, put it in the kiln, until you're done for the day.
I'm a little pressed for time right now, or I'd address more of your questions. My best bit of advice for you is to get a good book on flameworking. There are a few out there, and they'll give you so much great info!
__________________
High-temp, military grade 1/4" hollow mandrels are now available in my Etsy shop!
I have 12" and a limited number of 9" ready to go! BULK PRICING AVAILABLE
Also Available in To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. : my Electroforming for Everyone booklet.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2007-12-30, 6:33pm
|
|
Ellyloo-YAH!
|
|
Join Date: Aug 01, 2006
Location: Port Colborne
Posts: 2,775
|
|
Hi!
This is what I do.
My kiln is right beside me as I torch.
I ramp my kiln up to 960 as fast as is healthy for my kiln (some say top speed stresses the kiln out, some say it doesn't... I just do it fast enough to get there within the hour)
Hold for as long as you want to torch, plus 30 mins or so.
I set it to ramp down to 840 at 100 degrees/hr.
I set it to hold for about 45 mins, (some do for much less, but i like to be double darn sure of annealing, and this covers any 'larger' pieces I may make)
After that, how slow you ramp down is up to you....I kinda forget what my kiln is programmed to do, I think it stops at 500 again for 20 mins, and then goes down to 200 and shuts off. It takes mine all night, i don't mind going slow.
Torch! When you deem your bead as "DONE" (large or small) --place it into the kiln.
Keep it up!
When your kiln is down to the last 30 mins, you're done.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2007-12-30, 9:12pm
|
|
Life is change. Love it
|
|
Join Date: Oct 10, 2005
Location: Ontario Canada
Posts: 5,566
|
|
Elly, I think all of us in S.Ontario have the same annealing schedule. That is so funny!
__________________
cRlyn, cause Traci says so
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2007-12-30, 9:38pm
|
|
Senior Member
|
|
Join Date: Sep 01, 2007
Location: Greenville, SC
Posts: 1,749
|
|
Another thing to consider: the type of glass you're using dictates the annealing temp. Do some research on this and other forums and you'll find there's TONS of information out there. Tink and some others have been working on a chart for annealing various types of glass. http://www.lampworketc.com/forums/sh...aling+schedule
This will give you some good information. As you research, prepare to be overwhelmed. Then take a deep breath and dive in! You'll figure it out as you go. Have fun!!
__________________
~Rachel
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2007-12-30, 9:46pm
|
|
Ellyloo-YAH!
|
|
Join Date: Aug 01, 2006
Location: Port Colborne
Posts: 2,775
|
|
Quote:
Originally Posted by Carolyn M
Elly, I think all of us in S.Ontario have the same annealing schedule. That is so funny!
|
It is!
Annealing Culture.
Different dialects for different parts of the country....
It probably means we all learned it from the same group of people.
(some more down the line than others).
I want to be extra sure I"m okay, especially if i'm doing something in the winter...can't hurt to soak longer, or twice, or ramp down slower..... *shrug*
PS: Oh yes.... and about the types: yes! I dabbled with Satake once, and decided not to dabble more, because I didn't want to change my schedule all around... and I know that once I start dabbling with Boro I'll have to change things (higher)
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2007-12-31, 9:10am
|
|
one day at a time
|
|
Join Date: Jun 27, 2005
Location: We are MOVING!!!
Posts: 8,319
|
|
Elly, my schedule is very similar to yours! But I thought my kiln was running a little too hot on hold time, so I have it set at 940 for garaging.
Yes, I agree all beads should be annealed, even tiny spacers.
__________________
You live in a world of money. Money means choices. No money, no choices. Welcome to reality.
Melody (Marlee Matlin) from Switched at Birth
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -7. The time now is 7:06am.
|