Default Always with the cracking!

Errrgh...

Hi people, I've got another newbie problem. All of my beads are cracking. Almost every single bead I've made has cracked in the kiln, and it has gotten progressively worse since I started working. What am I doing wrong? I've made about seven marbles, none of which have cracked. I also threw together two really weird little figurines and one of those cracked. Am I not putting them in soon enough? I haven't heard, seen, or felt any of the beads crack before putting them into the kiln.

I use a minor torch, a Chilli-pepper, Moretti and Vetro glasses, aaaand.... that's it.

Help!

Thanks guys,
Cowboy
__________________
Check out my sculptures and other work!

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.

The Big Purple Barn is a big, beautiful dream.
Reply With Quote
  #2  
Old 2012-09-16, 10:31am
Eileen's Avatar
Eileen Eileen is offline
Loving learning
 
Join Date: Oct 11, 2010
Location: Florida
Posts: 11,699
Default

Can you post a picture of the cracked beads? Are they cracking along the mandrel, or zig zag through the bead?
Reply With Quote
  #3  
Old 2012-09-16, 10:38am
bigpurpleb bigpurpleb is offline
Member
 
Join Date: Sep 06, 2012
Location: In the past.
Posts: 31
Default

I'll try and get a picture. Some are cracking at the ends, around the hole through the bead. Others are splitting in halves or thirds along the direction of the mandrel. The ones that crack at the ends stay together otherwise and the ones that split completely have smooth breaks.
__________________
Check out my sculptures and other work!

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.

The Big Purple Barn is a big, beautiful dream.
Reply With Quote
  #4  
Old 2012-09-16, 10:48am
Polgarra's Avatar
Polgarra Polgarra is offline
Nikki Haverstock
 
Join Date: Oct 10, 2010
Location: NW Colorado
Posts: 1,686
Default

It might help to describe your procedure as you torch.

Once you are done how long until you put it in the kiln? How hot is the kiln? What glass are you using? The more details the more likely you will get helpful advice.
__________________
Nikki Haverstock

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Reply With Quote
  #5  
Old 2012-09-16, 10:51am
Eileen's Avatar
Eileen Eileen is offline
Loving learning
 
Join Date: Oct 11, 2010
Location: Florida
Posts: 11,699
Default

From what I've read, the ones cracking in half, thirds, etc. along the mandrel got too cool before you put them into the hot kiln.
Do you hold them out just until they lose the orange glow, then pop them in the not kiln?
Reply With Quote
  #6  
Old 2012-09-17, 5:35pm
Dasi's Avatar
Dasi Dasi is offline
Senior Member
 
Join Date: Aug 27, 2005
Location: Florida
Posts: 2,186
Default

Are you keeping the bead nice and hot with insurance heat while you are working on a bead? You can't let the heat go out of certain parts of the bead while working on other areas. Make sure the heat is equaled in the bead before you put it in the kiln.
__________________
Heather Ferman Web site:
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.

Viking knit End Caps for sale:
[/url]https://heatherferman.etsy.com[/url]
Reply With Quote
  #7  
Old 2012-09-17, 7:29pm
Molly Bird's Avatar
Molly Bird Molly Bird is offline
Senior Member
 
Join Date: Oct 26, 2011
Location: Amarillo, TX
Posts: 254
Default

Have you made sure your annealing schedule is correct? Maybe they are cooling too fast in the kiln. I anneal at 968-973 & after the last bead goes in, I give it an additional 30 minutes soak time (I usually make about 12mm beads.) I ramp down to 800 at 150 degrees an hour and hold for 45 minutes, then ramp down at 350 degrees per hour to 350then shut off. This is probably ultra conservative, but it works for me. I think cooling too fast is the main reason beads crack.
Reply With Quote
Reply

Tags
cowboy, cracking, question, soft glass


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Forum Jump




All times are GMT -7. The time now is 6:16pm.


Powered by vBulletin® Version 3.7.5
Copyright ©2000 - 2024, Jelsoft Enterprises Ltd.
Your IP: 18.207.160.209