Default Brass or Graphite press

Which do you like the best brass or graphite press? Pros and cons please. I am getting ready to order and am conflicting between the two.
Reply With Quote
  #2  
Old 2019-05-23, 8:56am
echeveria's Avatar
echeveria echeveria is offline
Senior Member
 
Join Date: Aug 31, 2006
Location: Knoxville, TN
Posts: 1,909
Default

I use both, and both are fine. If you think you are prone to dropping them or dropping stuff on them, get brass.
__________________
Kathy
Reply With Quote
  #3  
Old 2019-05-23, 1:47pm
Sudsy Sudsy is offline
Member
 
Join Date: May 11, 2009
Posts: 44
Default

Thanks you. I have brass presses and was wondering if there was an advantage to using graphite press.
Reply With Quote
  #4  
Old 2019-05-23, 2:03pm
beadmama's Avatar
beadmama beadmama is offline
Senior Member
 
Join Date: Sep 22, 2006
Posts: 1,133
Default

Good and bad in both ....brass Will tarnish. I do think the graphite can chip easily on the corners. I had 2 that chipped in the corner near the peg hole. I didn’t drop it either. The press is usable but if brass is offered I would go that route instead. I do like graphite beadrollers and had a couple spacer ones break from dropping them. JMHO
__________________
Becky
Reply With Quote
  #5  
Old 2019-05-29, 1:52pm
rainygrrl's Avatar
rainygrrl rainygrrl is offline
dances with ideas...
 
Join Date: Sep 15, 2005
Location: Rochester, MN
Posts: 2,278
Default

Brass will “grab” the glass a bit; graphite won’t.
__________________
Roberta
"Excels at making things more complex than they need to be"

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Reply With Quote
  #6  
Old 2019-05-31, 6:54am
yonil's Avatar
yonil yonil is offline
Senior Member
 
Join Date: Feb 14, 2009
Location: New Hampshire
Posts: 378
Default

I like to use brass when working with a glass that has reactions with extreme hot to cold changes. Like raku--Heat up the raku, then press it with a brass shaper, to cool it fast and get extra color out. Or if I want the glass I added to be pushed down but not spread so much, I'll use the brass, because it's more likely to "freeze" the glass in place rather than spread it out.

I like the graphite for gentle shaping where I want the glass to move a bit more.

I use both a lot!
Reply With Quote
  #7  
Old 2019-06-13, 7:05pm
Mountain Snail's Avatar
Mountain Snail Mountain Snail is offline
Senior Member
 
Join Date: Oct 08, 2010
Posts: 855
Default

I prefer brass. Graphite is great for marvering but I like brass for smooshing.
Reply With Quote
Reply


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Forum Jump




All times are GMT -7. The time now is 12:23pm.


Powered by vBulletin® Version 3.7.5
Copyright ©2000 - 2019, Jelsoft Enterprises Ltd.
Your IP: 100.24.122.228