Question Keeping Parts Warm

I'm only about a month into lampworking and I'm slowly gaining knowledge and skill. I have a nice torch (Nortel Major/Minor) and a small kiln (Jen-Ken Chili Pepper) for annealing. So far, I'm using soft glass (104 COE) and making small objects.

Question: When making objects with that require multiple pieces to be joined together, how do people keep a part warm while making other parts? Should I just put them in my kiln or is there another option where they're a bit easier to access when needed? I watch videos of the pros demonstrating in Corning and elsewhere and never really see how they manage this aspect of the art...
Reply With Quote
  #2  
Old 2022-10-25, 1:23pm
rcktscientist rcktscientist is offline
Senior Member
 
Join Date: Jun 19, 2021
Location: los angeles
Posts: 154
Default

The term most use is to "garage". As in, "I'll garage this part while I make the other part, then join them together"
Yes, a kiln is one of the best ways to garage parts. Some people actually use the top of the kiln to keep pieces warm but I'd recommend inside the kiln for COE104.
Also, some people adjust their workflow and simply keep the first piece warm by flashing after adding parts directly, always keeping the temp above the strain point (about 850F for soft glass).
__________________
Bobcat on 15lpm and Phantom on HVLP
Reply With Quote
  #3  
Old 2022-10-25, 2:53pm
mattreidy mattreidy is offline
Junior Member
 
Join Date: Oct 25, 2022
Posts: 2
Smile

Quote:
Originally Posted by rcktscientist View Post
The term most use is to "garage". As in, "I'll garage this part while I make the other part, then join them together"
Yes, a kiln is one of the best ways to garage parts. Some people actually use the top of the kiln to keep pieces warm but I'd recommend inside the kiln for COE104.
Also, some people adjust their workflow and simply keep the first piece warm by flashing after adding parts directly, always keeping the temp above the strain point (about 850F for soft glass).
I've moved my kiln closer to my torch so I can move pieces in/out now so I'll give the garaging method a try. Thanks!
Reply With Quote
  #4  
Old 2022-10-25, 3:29pm
ESC ESC is offline
Senior Member
 
Join Date: Feb 02, 2010
Posts: 3,473
Default

In the past I used a glass top buffet warmer, but rcktscientist is right. If you can keep the parts warm in the kiln, they're going to be much less likely to shatter when reintroduced to the flame.
__________________
ESC
Soft glass on a Minor/concentrator since 1996
Reply With Quote
  #5  
Old 2022-10-31, 6:37pm
rainygrrl's Avatar
rainygrrl rainygrrl is offline
dances with ideas...
 
Join Date: Sep 15, 2005
Location: A map dot in Montana
Posts: 2,388
Default

Agree that a kiln is best but for convenience when working with small parts, a hot plate can work. For example, if I’m building a complex floral murrini I would heat petal pieces (about 1 inch long by 4 or 5 mm in diameter) on my hot plate. You have to be careful hen introducing to the flame, of course.
__________________
Roberta
I think I've lost the plot...

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Reply With Quote
Reply

Tags
annealing, soft glass


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Forum Jump




All times are GMT -7. The time now is 9:35am.


Powered by vBulletin® Version 3.7.5
Copyright ©2000 - 2024, Jelsoft Enterprises Ltd.
Your IP: 44.211.34.178