Tips, Techniques, and Questions -- Technical questions or tips |
2013-04-09, 8:35am
|
Senior Member
|
|
Join Date: Jan 22, 2012
Location: Florida
Posts: 591
|
|
surface bubbles on pressed beads
I was hoping someone could help me out with this. Maybe Gems, since the twistie recipes where hers (they are wonderful by the way). I am on a hothead, so that needs to be know. I will also try and photograph the problem. When I initially make the bead all is fine, however, when I shape the lentil and the got to fire polish I am getting bubbles tiny bubbles and I can't seem to get them out. So basically ruining the beads. Am I trapping air?, over heating? Any thoughts.
Thanks in advance,
Cherri
__________________
Life without art would be BORING!
ArtbyCherri.com
|
2013-04-09, 9:25am
|
|
Jacqueline Parkes
|
|
Join Date: Nov 04, 2005
Location: Vancouver, Canada
Posts: 4,497
|
|
Hmmm pictures would help as I am not sure which twisties etc you are using. Bubbles in the whole bead or just in the twisties? waiting on pictures
Which tutorial are you referring to?
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-04-09, 9:57am
|
Senior Member
|
|
Join Date: Jan 22, 2012
Location: Florida
Posts: 591
|
|
Here is a shot of the beads.
Thanks
__________________
Life without art would be BORING!
ArtbyCherri.com
|
2013-04-09, 10:00am
|
|
Jacqueline Parkes
|
|
Join Date: Nov 04, 2005
Location: Vancouver, Canada
Posts: 4,497
|
|
pitting = too much heat
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-04-09, 11:08am
|
|
I'm meeeeelting
|
|
Join Date: May 27, 2007
Location: Seattle, WA
Posts: 2,236
|
|
Also, some colors, such as black, don't like to be reheated without a chance to cool adequately in between.
__________________
Etsy: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Foot Pedal Tutorial: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Kevlar Fingerless Gloves: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-04-09, 11:10am
|
|
Jacqueline Parkes
|
|
Join Date: Nov 04, 2005
Location: Vancouver, Canada
Posts: 4,497
|
|
Yes I find Effetre black will pitt as well if not treated with TLC.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-04-09, 5:25pm
|
Senior Member
|
|
Join Date: Jan 22, 2012
Location: Florida
Posts: 591
|
|
Thanks no eff black
__________________
Life without art would be BORING!
ArtbyCherri.com
|
2013-04-12, 6:37am
|
|
ScrapSurfGlassPaddleSew
|
|
Join Date: Jan 22, 2012
Location: Upstate NY
Posts: 3,223
|
|
Yeah, I always think of that as boiling the glass. Sometimes it's really hard to firepolish without making a bigger mess.
__________________
Pat The journey is the reward To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. L-111
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-04-13, 12:13am
|
|
Slogan Challenged...
|
|
Join Date: Mar 21, 2009
Location: Maricopa, Arizona
Posts: 6,287
|
|
Quote:
Originally Posted by eregel
Yeah, I always think of that as boiling the glass. Sometimes it's really hard to firepolish without making a bigger mess.
|
This.
__________________
Kristin ~
Facebook: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Etsy: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2013-04-13, 1:06am
|
|
The Harbinger of Cuteness
|
|
Join Date: Dec 11, 2007
Location: Los Osos, San Luis Obispo County, California
Posts: 1,465
|
|
Quote:
Originally Posted by KJohn
This.
|
Double that.
__________________
Aimee Moisa
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. ~ To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. ~ To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. #M-191
|
2013-04-13, 1:54am
|
|
one day at a time
|
|
Join Date: Jun 27, 2005
Location: We are MOVING!!!
Posts: 8,319
|
|
It has been my experience that some glass does it and some doesn't. Same with frit.
__________________
You live in a world of money. Money means choices. No money, no choices. Welcome to reality.
Melody (Marlee Matlin) from Switched at Birth
|
2013-04-13, 6:53am
|
|
Senior Member
|
|
Join Date: Sep 18, 2005
Location: WA
Posts: 1,177
|
|
Quote:
Originally Posted by Lisi
It has been my experience that some glass does it and some doesn't. Same with frit.
|
Yep - I'm on a hothead too - esp when trying to get those delicious furnace glass colors on the surface. My hunch is that it elates to the amount of Mapp or somehow to the interaction at the border of the 104 and 96 coes.......doesn't seem to matter with me how slowly I melt the glass in........truly one of my biggest frustrations in all the time I've been making beads. There have been some batches of black that were plain impossible to melt without bubbling and black usually doesn't do this.
__________________
Vicki B.
~~~~~~~~~~~
On a Hot Head for 6 years! 1 lb MAPP canisters from Ace
|
2013-04-13, 4:43pm
|
|
one day at a time
|
|
Join Date: Jun 27, 2005
Location: We are MOVING!!!
Posts: 8,319
|
|
There was a bad batch of Vetrofond black way back in 2003 that was bubbly pitty horrible. Anything that I made bigger than 15mm would do that, and I was on the HH then.
__________________
You live in a world of money. Money means choices. No money, no choices. Welcome to reality.
Melody (Marlee Matlin) from Switched at Birth
|
2013-04-14, 5:32pm
|
|
Senior Moment
|
|
Join Date: Jun 16, 2012
Location: New Yawk
Posts: 4,161
|
|
Just wanted to add I'm on a HH using MapPro. There are some colors that just seem to loathe the fuel rich flame the HH kicks out. For me it's mostly teals (CIM Azure for example, pits like that from the word go, and Lauscha Bluetonium will do it if i let it cool a bit and reheat). Occasionally some greens will get pitty and of course EDP is her cranky self with the HH; I also have to be careful with Goldstone. Makes me wonder if copper is playing a role here.
Blacks, however, are well behaved for me ( I've probably jinxed myself LOL); CIM Hades, Tuxedo, Effetre Blacks, etc.
HTH a little!
Alli
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
I never finish anything. I have a black belt in partial arts.
|
2013-04-15, 7:54pm
|
Senior Member
|
|
Join Date: Jan 22, 2012
Location: Florida
Posts: 591
|
|
Well, I did not get back to the pressed beads.. drat.. Ran out of time, so now have to wait until next week to try again. I am sure that I just got them to hot. I know before I pressed all was great. Then When I pressed them, I think they were still ok, it was trying to do the final polish that I got into trouble. I think I may need to let them cool a bit more in between. If that does not do it, then will rethink the frits I used. I am going to give it a go though. I really liked the colors I got, just have to get it to play nice with me.
__________________
Life without art would be BORING!
ArtbyCherri.com
|
2013-04-21, 2:46pm
|
|
Senior Member
|
|
Join Date: Apr 03, 2013
Posts: 129
|
|
What's "pitting"? Does that mean part of the bead isn't round or a pit has formed in the surface?
|
2013-04-21, 6:29pm
|
|
The Harbinger of Cuteness
|
|
Join Date: Dec 11, 2007
Location: Los Osos, San Luis Obispo County, California
Posts: 1,465
|
|
Quote:
Originally Posted by PatsyEmporium
What's "pitting"? Does that mean part of the bead isn't round or a pit has formed in the surface?
|
That is when you get pits on the surface of the bead. Know what a adult who had really bad teenage acne looks like? With acne scars all over their face? That's "pitted". In lampworking you can get pitting from microbubbles you get from pressing then reheating your bead. The little bubbles form like almost microscopic acne on the surface of the bead then pop leaving ittybitty tiny scars. It's really quite ugly and happens very easily on certain colors. My particular nemesis is anything in the turqoise family. It pits if you look at it funny, and screams bloody murder if you press and then reheat (which you want to do to remove the chill marks). I've heard (but don't quote me) that it is caused by the metal molecules in the glass chilling more when pressed then the glass molecules do, then reheating the metals boils them off 'cause you're reintroducing those cold metal molecules too quickly to the flame. They boil, pop, then leave the horrible pits. Or something. Sounds logical to me.
Ooh, just had an idea... I've had a lot of luck sticking any old bead in the kiln to hold for a bit then bringing it back out and reintroducing it to the flame slowly to reheat it and do more work on it. Maybe I can make a turquoise bead, press it, put it in the kiln for a while to even out the temp, then put it back in the flame to fire polish (i.e. get rid of the chill marks) and continue working on it. Hmm, I will try that.
__________________
Aimee Moisa
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. ~ To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. ~ To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. #M-191
|
2013-04-22, 6:05am
|
|
Senior Member
|
|
Join Date: Sep 18, 2005
Location: WA
Posts: 1,177
|
|
Somehow it seems to happen in the last part of melting or polishing. I often get this when I melt murrini flat - I think especially if there is 96 coe in the murrini on 104 bead. Maybe it is metal particles on the surface as there is little sparking (I think). It really doesn't seem to matter how slowly I melt in...
__________________
Vicki B.
~~~~~~~~~~~
On a Hot Head for 6 years! 1 lb MAPP canisters from Ace
|
2013-04-22, 7:41am
|
|
The Harbinger of Cuteness
|
|
Join Date: Dec 11, 2007
Location: Los Osos, San Luis Obispo County, California
Posts: 1,465
|
|
Quote:
Originally Posted by Vicki B.
Somehow it seems to happen in the last part of melting or polishing. I often get this when I melt murrini flat - I think especially if there is 96 coe in the murrini on 104 bead. Maybe it is metal particles on the surface as there is little sparking (I think). It really doesn't seem to matter how slowly I melt in...
|
I agree, it doesn't seem to matter how slowly I reheat pressed turquoise either, but ONCE I decided to reheat it so slowly you would have thought I was in a race for slowest snail. That helped. I think it just needs to be "ridiculously slow" which I consider to be a waste of my time. I KNOW it needs to be done slowly, I just have other things I'd rather do with my time. :^)
It's probably also about flame chemistry too. Maybe "too slowly, with a little too much propane"? My flame's a bit propane rich 'cause my oxycon's a little on the tired side.
__________________
Aimee Moisa
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. ~ To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. ~ To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. #M-191
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments