I had an interesting question from a customer today. She asked what type of glass I used. I responded with soft glass, mostly Effetre, Moretti and CiM. She said that was good... she needed to know the types of glasses so she is sure there is no lead. She says she asks all lampwork artists the type of glass used.
I know we have to have good ventilation for our own protection, but once the glass is made, could lead still be a danger to custsomers?
__________________
~Trish
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
follow me on Instagram @tinkercreekcreations
|
2014-04-07, 6:26pm
|
|
Senior Member
|
|
Join Date: Aug 01, 2005
Posts: 2,159
|
|
The danger isn't necessarily from absorbing lead. The more immediate problem is the legal implication of having lead on the surface of the glass. Check the CPSIA. Rubino Oro, EDP and most reduction frits leave a thin layer of lead on the surface. This can look like gold, silver or an assortment of colors depending on the thickness of the layer and the size/distribution of the particles (often in the 1 micron size). Lead is a problem and bead makers need to recognize it.
Robert
__________________
Robert Simmons
(Former) Director for Bead Donations
Beads of Courage, Inc.
|
2014-04-07, 7:05pm
|
Senior Member
|
|
Join Date: Jun 26, 2013
Location: Roanoke, Va
Posts: 432
|
|
Thank you Robert. This is good to know!
__________________
~Trish
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
follow me on Instagram @tinkercreekcreations
|
2014-04-17, 11:30am
|
|
Junior Member
|
|
Join Date: Oct 13, 2013
Location: Athens, Greece
Posts: 14
|
|
if in the surface of the glass there are is this thin layer, then this may be subjected to chemical reaction with air; so happens with coatings, most silver base, that they used to float glasses.
general speaking, can this layer reacts with the environment, i ask because i know that the glass is neutral to the most of the chemicals.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Aude sapere.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2014-04-17, 4:27pm
|
Senior Member
|
|
Join Date: Feb 02, 2010
Posts: 3,382
|
|
Robert, is this a real danger after the bead is made though? Unless you have the bead in your mouth for long periods or you're making a vessel that will contain liquid that could leach the lead out over time, wouldn't it just sit on the surface of the glass.
I would think the biggest danger would be when the glass is molten and the lead is volatilized (big reason to have ventilation) in the flame. I mention this because years ago, Vince cautioned me against fuming glass with EDP. All the pretty colors were the lead coming out of the EDP and depositing on the bead.
ESC
|
2014-04-17, 8:25pm
|
|
Artistically Absorbed
|
|
Join Date: Jul 27, 2007
Location: Emerald City
Posts: 546
|
|
I think if it is encased there is no more danger, but I could be wrong.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. Believe in Yourself and Anything is Possible! To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. SRA Artist A64
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -7. The time now is 12:24pm.
|