Temperature or incompatibility? The wisdom of LE I need you!
Making a fan pull as a housewarming gift for a friend. Made and annealed the focal piece last week and it was fine; picked it up last night and noticed...cracks. Auuggghh!
(sorry bout the horrible pics; forgot the camera was still set for the eclipse photos)
I'm unsure if the cracks are due to temp issues (it's a big heart; 2 full rods just for the base, so maybe it got a little cool when I was adding the decor?), or incompatibility (which would be weird; the base is just CIM Mojito over Effetre Clear and all decor is 104 and used in other beads without issue, but the cracks look to me like incompatibility). Thing is, the colors are pretty close to her wall/furniture colors in the room the fan pull would be in. If it's a temp issue, well, friggin hell, but I can redo. If it's compatibility, I'll have to rethink all my colors ($^&@#*%!).
Opinions please!!
Alli
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
I never finish anything. I have a black belt in partial arts.
|
2015-10-09, 7:38pm
|
|
Loving learning
|
|
Join Date: Oct 11, 2010
Location: Florida
Posts: 11,654
|
|
I don't know on the reason, but can you put it back on a coated mandrel, heat it in the kiln, and try to heal the cracks & see what happens? ( slowly slowly since it is so big)
__________________
My current "hot" fantasy involves a senior discount on glass & tools!
|
2015-10-09, 7:43pm
|
|
Senior Moment
|
|
Join Date: Jun 16, 2012
Location: New Yawk
Posts: 4,161
|
|
LOL It's such a damn big bead I'd be afraid to Eileen; I'd probably have a heart attack if it decided to blow apart when reintroduced to the flame.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
I never finish anything. I have a black belt in partial arts.
|
2015-10-09, 7:49pm
|
|
Loving learning
|
|
Join Date: Oct 11, 2010
Location: Florida
Posts: 11,654
|
|
That would smart if any pieces landed on you for sure!
__________________
My current "hot" fantasy involves a senior discount on glass & tools!
|
2015-10-09, 8:29pm
|
|
member
|
|
Join Date: Nov 24, 2006
Posts: 524
|
|
With them wandering around not in a straight line, it looks more like incompatibility than thermal cracks. That's too bad.
|
2015-10-09, 8:39pm
|
|
da General
|
|
Join Date: Oct 05, 2006
Location: San Francisco
Posts: 13,002
|
|
Sorry to say it looks like incompatibility, Alli! CiM may be the culprit. Sometimes glass combination may work in smaller beads when they are slightly incompatible but cracks on larger beads... Ask me how I know! Lol!
__________________
Hayley
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. | To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. | To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. | To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. | To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2015-10-10, 7:42am
|
|
Loving learning
|
|
Join Date: Oct 11, 2010
Location: Florida
Posts: 11,654
|
|
Maybe Effetre olive green instead?
__________________
My current "hot" fantasy involves a senior discount on glass & tools!
|
2015-10-10, 9:02am
|
|
Corgi Cult Member
|
|
Join Date: Jan 10, 2006
Location: Central Illinois
Posts: 3,723
|
|
Could you skip the clear and use solid mojito? I know it would be cost more, but you don't have a huge amount of decoration and the cracks don't seem to follow the decoration, so the problem may be the mojito over clear.
I find more cracking problems in really big hearts with vertical holes. The mandrel is a heat sink, then it looses more heat because of the crease. Each lobe of he heart is still large, so they retain more heat. Before putting in the kiln, I try to equalize the heat in the piece. The larger they are, the harder it is, IMO.
We often think of cracks as either incompatibility or thermal, but I often wonder if inconsistent heat doesn't aggregate incompatibility. Just my opinion though.
__________________
Kathy
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2015-10-10, 2:56pm
|
|
hyperT
|
|
Join Date: Jan 31, 2013
Location: San Antonio, Texas
Posts: 582
|
|
10 minutes held at the annealing point per millimeter thickness. Mt. Palomar telescope lens took 10 months to bring down to room temperature. They blew the first lens by cooling to fast.
This is especially important in thicker pieces. 25.4 mm = 1 inch x 10 = 254 minutes held at the annealing point. When the temperature reaches down to 500 degrees F you can vent the oven a bit
and cool faster.
|
2015-10-10, 7:20pm
|
|
Slogan Challenged...
|
|
Join Date: Mar 21, 2009
Location: Maricopa, Arizona
Posts: 6,287
|
|
I can see how the size would mean a slower ramp down time, that sounds like a big bead. Isn't a clear core the usual advice for glass that doesn't like to be encased? If it was a core of Mojito, I can see that being a problem. Those do look like incompatibility cracks to me too, that would definitely be my first thought. Sorry for all that work, it is a lovely piece!!
__________________
Kristin ~
Facebook: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Etsy: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2015-10-10, 8:29pm
|
|
Senior Moment
|
|
Join Date: Jun 16, 2012
Location: New Yawk
Posts: 4,161
|
|
Poop poop poop. Yeah, I can try to remake with just a Mojito core, assuming my last 2 rods of it are enough. I initially cored it with clear so I would have some Mojito for the smaller beads; there goes that plan LOL. And I can easily up the annealing time. While I've made others this big and they've been fine, I do NOT want to do the same-ish bead for a 3rd time (I get bored easy and have such a short attention span...oh look! A light!).
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
I never finish anything. I have a black belt in partial arts.
|
2015-10-11, 4:25am
|
|
hyperT
|
|
Join Date: Jan 31, 2013
Location: San Antonio, Texas
Posts: 582
|
|
Putting a coin in front of the wood base would give us a reference to the size of the bead.
|
2015-10-11, 5:18am
|
|
Slogan Challenged...
|
|
Join Date: Mar 21, 2009
Location: Maricopa, Arizona
Posts: 6,287
|
|
Oh look, a squirrel!
You know, come to think of it, way back when I had a hothead and was cooling in a fiber blanket to batch anneal......I did some larger beads that had cracks like that along the side. It turns out they were hitting each other in the blanket, or too close and the hotter one would crack the cooler one, or vice versa. Also I might not have been heating evenly before I put them in.
So it may indeed be temperature related, as Kathy said it needs to be heated evenly. Was anything else in the kiln?
__________________
Kristin ~
Facebook: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Etsy: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2015-10-11, 7:36am
|
|
Senior Moment
|
|
Join Date: Jun 16, 2012
Location: New Yawk
Posts: 4,161
|
|
Hrmm. I am using a HH, but everything goes directly into the kiln and this puppy was in there all by its lonesome, so not affected by other bead temps.
And this is another bead made with the same press for size reference:
Squirrel? Squirrel?! SQUIRREL!
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
I never finish anything. I have a black belt in partial arts.
|
2015-10-11, 8:17am
|
|
Loving learning
|
|
Join Date: Oct 11, 2010
Location: Florida
Posts: 11,654
|
|
Oh wow, that is much bigger than I thought. How long did you anneal it for before beginning the temp drop, and how fast did you drop it?
__________________
My current "hot" fantasy involves a senior discount on glass & tools!
|
2015-10-11, 8:40am
|
|
Phill
|
|
Join Date: Mar 21, 2009
Location: Winnebago, MN
Posts: 2,489
|
|
I am going to guess thermal cracking now that you have mentioned the press.
Presses suck the heat of the glass fast than a Jedi Knight reacts to a light saber and getting the heat back into it with a hot head torch is going to take the patience of a Saint and the heat control of Oby Won himself as well as triple or quadruple the kiln soak and ramp down time of anything I have ever worked with or imagined.
__________________
The Zombie Apocalypse is Upon Us.
|
2015-10-11, 11:22am
|
|
Slogan Challenged...
|
|
Join Date: Mar 21, 2009
Location: Maricopa, Arizona
Posts: 6,287
|
|
See now, that is the fun of lampworking, you get to be all sorts of cool people!
__________________
Kristin ~
Facebook: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Etsy: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2015-10-11, 3:27pm
|
Senior Member
|
|
Join Date: Sep 27, 2014
Location: Walla Walla, Washington
Posts: 289
|
|
Id try it in boro. Its not near as fussy.
|
2015-10-11, 3:59pm
|
|
Senior Moment
|
|
Join Date: Jun 16, 2012
Location: New Yawk
Posts: 4,161
|
|
Quote:
Originally Posted by snoopdog6502
Id try it in boro. Its not near as fussy.
|
LOL Ever try to melt boro with a HotHead? I'd be still trying to melt the same rod from the nursing home.
Gonna give it another go tonight. Got the kiln annealing time changed and will try a diff combo *fingers crossed*
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
I never finish anything. I have a black belt in partial arts.
|
2015-10-11, 4:15pm
|
Senior Member
|
|
Join Date: Jun 11, 2005
Posts: 1,880
|
|
Make it hollow! Way less glass and sturdier.
|
2015-10-16, 9:35am
|
|
Pincel de Fuego
|
|
Join Date: May 18, 2010
Location: Panama city, Panama
Posts: 406
|
|
Quote:
Originally Posted by beadbroad
Make it hollow! Way less glass and sturdier.
|
How DAFUQ do you make a hollow heart!?!!!!
__________________
Gabi
Pincel de Fuego
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. / To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. / To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2015-10-16, 9:36am
|
|
Pincel de Fuego
|
|
Join Date: May 18, 2010
Location: Panama city, Panama
Posts: 406
|
|
By the way! Hi Alli! Miss you...
I'm so glad to s
Squirrel!
__________________
Gabi
Pincel de Fuego
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. / To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. / To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2015-10-16, 10:04am
|
|
hyperT
|
|
Join Date: Jan 31, 2013
Location: San Antonio, Texas
Posts: 582
|
|
Quote:
Originally Posted by GabiLoraine
How DAFUQ do you make a hollow heart!?!!!!
|
You melt the end of a tube into a gather and blow it into a two part mold.
Then cut it off the end like a Christmas bulb.
Good luck with that.
|
2015-10-16, 10:24am
|
|
Pincel de Fuego
|
|
Join Date: May 18, 2010
Location: Panama city, Panama
Posts: 406
|
|
Quote:
Originally Posted by hyperT
You melt the end of a tube into a gather and blow it into a two part mold.
Then cut it off the end like a Christmas bulb.
Good luck with that.
|
Oh of course. On a HH.
Lol.
__________________
Gabi
Pincel de Fuego
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. / To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. / To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2015-10-16, 10:31am
|
|
Senior Moment
|
|
Join Date: Jun 16, 2012
Location: New Yawk
Posts: 4,161
|
|
Squirrel? Squirrell?! *grin* Good to see you girl (love the new avatar pic...ooooo, a light!).
And yeah, trying to make it hollow requires more coordination and dexterity than I'm able to muster LOL I'm going to to the stringer test to check compatibility (why this never occurred to me before, I haven't the vaguest idea). Then I'll have a better idea if it's compatibility or temp.
Alli
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
I never finish anything. I have a black belt in partial arts.
|
2015-10-16, 12:21pm
|
|
hyperT
|
|
Join Date: Jan 31, 2013
Location: San Antonio, Texas
Posts: 582
|
|
Quote:
Originally Posted by GabiLoraine
Oh of course. On a HH.
Lol.
|
ok so you blow a bubble and crease it with a knife. The trick here is to blow a uniform starter bubble so the wall thickness is uniform.
What's a HH lol
|
2015-10-16, 3:54pm
|
|
Senior Moment
|
|
Join Date: Jun 16, 2012
Location: New Yawk
Posts: 4,161
|
|
Quote:
Originally Posted by hyperT
What's a HH lol
|
A HotHead torch
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
I never finish anything. I have a black belt in partial arts.
|
2015-10-19, 9:56am
|
|
Queen of the milo field
|
|
Join Date: Jul 30, 2012
Location: In the middle of US and the middle of forty acres
Posts: 1,885
|
|
Quote:
Originally Posted by hyperT
What's a HH lol
|
A Hellacious Heathen?
dj
__________________
Dance all you want, but keep one hand on the wheel.
Sometimes I swim, sometimes I sail, but mostly I just try to stay afloat.
|
2015-10-22, 3:14pm
|
Naysayer
|
|
Join Date: Sep 22, 2009
Posts: 1,203
|
|
Mojito is one of my favorites, I make big honking beads, some 2 inches across. I usually always layer it over a core since it's semi expensive.
I know that doesn't help at all, I would just try more heat insurance.
|
2015-11-03, 6:37am
|
|
Senior Member
|
|
Join Date: Aug 27, 2005
Location: Florida
Posts: 2,186
|
|
I am sure it is a compatibility problem with the glass but you could just heat it up and heal the cracks and see if it cracks again......
I did a tutorial a LOOOOng time ago. Here is the thread on how to prepare beads to go back into the kiln and heal problems with beads....
http://www.lampworketc.com/forums/sh...g+broken+beads
__________________
Heather Ferman Web site: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Viking knit End Caps for sale:
[/url]https://heatherferman.etsy.com[/url]
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -7. The time now is 7:15am.
|