Originally Posted by likes to make glass stuff
That statement was referring to the shattering rods, lol, which most handpulled glasses do-especially the odd lots
Cracking happens-due either to user error, just because, or that there's a trick to it (encasing moretti/vetro reds anyone?).
|
I am sorry.I beg to differ. All of my Lauscha is hand pulled and it doesn't "shatter." Are you referring to thermal cracking with thicker rods when the are not preheated?
Paula
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Still North America's Largest Lauscha Dealer!
Now reopened in South Florida!!
Like US on Facebook ! To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-02-27, 4:29pm
|
|
Senior Member
|
|
Join Date: Sep 05, 2008
Location: Michigan
Posts: 391
|
|
Jack I love the pen beads, especially the last one..
Olga your beads are lovely, I really like the twisty on your third picture!
Michelle
__________________
*Michelle L*
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-02-27, 4:59pm
|
|
Senior Member
|
|
Join Date: Sep 12, 2007
Location: Haliburton
Posts: 81
|
|
Okay I don't get this. If lauscha is indeed 104 coe and is supposed to be compatible with all 104's why does it need to be annealed at 980, when the recommended anneal temp for all other 104 is 968 ?
Does that not stand to reason then that we have no idea what the coe of Lauscha is?
Does to me....sorry but the above reasoning makes no sense at all to me.
I have had many Lauscha beads crack on me and most had silver in them and others had copper mesh. Not something I can afford to waste and will no longer use any Lauscha for encasing or to combine with my 104's.
Seems the only common thing here with cracking is using silver with 104 glass and then adding lauscha to the mix, at least thats what I get when I did a seach of this issue.
Ah anyway, the beads are great and and I am still really really liking that salmon!
J
|
2009-02-27, 5:03pm
|
|
I fart diamonds
|
|
Join Date: Jun 14, 2005
Location: Altamonte Springs, FL
Posts: 3,893
|
|
Ok. Can we please stick with the topic of this thread? Devardi Glass?
__________________
-Shawnette the original "everybody get a grip" girl
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-02-27, 5:41pm
|
Senior Member
|
|
Join Date: Feb 06, 2009
Posts: 501
|
|
Quote:
Originally Posted by PaulaD
I am sorry.I beg to differ. All of my Lauscha is hand pulled and it doesn't "shatter." Are you referring to thermal cracking with thicker rods when the are not preheated?
Paula
|
ok, first off-I haven't even used Devardi.
Second-I'm throwing chocolate to you and backing off slowly
I was replying to a post that said they weren't going to use the glass due to shattering rods and cracking beads.
I think every single one of us can think of various colors of glass that shatter down the rod no matter what you do. Opal yellow and EDP come to mind right off the bat. I've read that many of the odd lot colors do this too. Some of it is certainly due to failure to preheat thicker rods (user error). Some of it is due to long bubbles running down the glass. Some of it just hates us and will shatter when we melt it no matter what we do.
Cracking beads-some glass just cracks when mixed with other glass-unless you know the "trick". Higher annealing temp for Lauscha, a wrap of clear underneath the moretti/vetro red/orange/yellow you intend to encase. There's also glass out there that you can't mix much at all-opalinos or alabastros, I can't remember which, but not only are the rods a PITA to use, but if you mix them much they crack. I use them for single color spacers, since I can't remember which is which with that, when I'm in the mood to duck flying pieces of glass.
I'm reading this thread because I intend to buy the glass when the next batch comes in. I want a heads up on the tricks and tips with it. I'll have to reinvent the wheel on some of it, just because that's my nature, but I really don't like seeing logic that doesn't follow ie: "I'm not buying it because the rods shatter and beads crack". Plus the fact of the most recent cracked bead being from a person who hasn't annealed them yet, and used lauscha clear for encasing-you can't blame the devardi alone for cracking, there are too many other plausible causes for the cracking.
|
2009-02-27, 5:42pm
|
|
Ad astra per aspera
|
|
Join Date: Jun 15, 2005
Location: Apache Junction AZ
Posts: 7,324
|
|
Just thought I'd report in (because I still have a touch of cynicism) that all of the beads I've posted in this thread are still intact. Woo!
ETA: That means they're all at least 3 weeks old.
__________________
Karen Sherwood
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-02-27, 5:51pm
|
|
On A Lampwork Hiatus
|
|
Join Date: Aug 30, 2005
Location: Daytona Florida
Posts: 1,427
|
|
All mine are still intact too minus the 1 that had a thermal and clear crack right out of the kiln. Going to play some more with it tomorrow.
|
2009-02-27, 10:48pm
|
|
Senior Member
|
|
Join Date: May 23, 2006
Posts: 5,540
|
|
Mine are good too! Jack, I love the second bead you have pictured there! I think I might need to order smore metalic black! I also need to get back to the torch and do some more stuff with the Davardi. I have been so busy. I'm so glad I get to see pics and read your comments too.
Thanks for all of your imput. I think it is very helpful to those who would like to try the glass.
__________________
Cynthia
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-03-01, 9:19am
|
|
Senior Member
|
|
Join Date: Sep 12, 2007
Location: Haliburton
Posts: 81
|
|
Ah you guys are killing me. I went to order some and all the colors I like are sold out!
I will be stalking the site from now on...LOL
J
|
2009-03-01, 12:31pm
|
Senior Member
|
|
Join Date: Aug 02, 2008
Posts: 116
|
|
I hear it will not be long before all the new colors will be in.
Jim
|
2009-03-01, 9:01pm
|
|
Just me
|
|
Join Date: Jun 27, 2005
Location: Tri-Cities-the armpit of Washington
Posts: 1,985
|
|
Does anyone have any bead pictures or can share their experience with that dark rose color I totally missed out on?
I would love to hear about it and see how it compares to rubino.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-03-01, 10:42pm
|
|
Ad astra per aspera
|
|
Join Date: Jun 15, 2005
Location: Apache Junction AZ
Posts: 7,324
|
|
I wish! The only thing close to pink I got was the salmon color.
__________________
Karen Sherwood
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-03-02, 10:52am
|
|
Just me
|
|
Join Date: Jun 27, 2005
Location: Tri-Cities-the armpit of Washington
Posts: 1,985
|
|
Well somebody bought it all!
Lets hope just one of them posts to this thread to make us all jealous.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-03-04, 7:09pm
|
|
Senior Member
|
|
Join Date: Sep 12, 2007
Location: Haliburton
Posts: 81
|
|
Yes I have been waiting to see how those pinks look as well. Love Rubino, but the price is tough to swallow and the fact I can't see the gold, kinda bugs me...lol
Yeh so I want big chunks of Gold! Who doesn't?
J
|
2009-03-04, 9:56pm
|
|
Senior Member
|
|
Join Date: Jun 27, 2005
Location: Yarmouth, Maine...home of the Clamfest
Posts: 7,693
|
|
No pictures, but my metallic black bead (yeah, it's not pretty & my camera is *still* at my sis's house 80 miles away--I'm an idiot) with striking glass color silver glass is still in PERFECT shape after a month of total abuse (smashing around in a baggie with 3 other beads in my coat pocket!)--it's got a melted in spot of striking color on one side & a round raised ball (like a gazing ball) on the other side, that's perfectly adhered still
No cracks, no weirdness, still a "stable" bead....
__________________
And if I laugh at any mortal thing, ‘Tis that I may not weep...” ~Lord Byron
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
new purple cricket @ home! minicc @ playing with fire in rockland! Sue & Nikki fighting over who gets to anneal the wonkies To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-05-07, 12:17pm
|
Junior Member
|
|
Join Date: Sep 14, 2005
Posts: 3
|
|
Looks like you can sign up for their newsletter and be informed as soon as the glass comes in.
|
2009-05-07, 7:17pm
|
|
Tacki
|
|
Join Date: Oct 26, 2008
Location: DFW, TX
Posts: 1,543
|
|
I'm an idiot... wrong thread...
|
2009-06-16, 6:16am
|
|
Formerly Deesigned Beads
|
|
Join Date: Aug 29, 2006
Location: Cape town, South Africa
Posts: 612
|
|
I've been chatting to Shawnette this past week or what about Devardi glass. The more I read and see, the more I get ants in my pants to try this glass out. The semi-opaques really draws me, and I guess I will start with that.
Furthermore, I make huge honking big beads - easily use 2 rods per bead ... So using this glass as a centre to save on my more expensive glass seems a good option.
I guess that my first order is looming, lol. Thank you for all the positive and negative thoughts, and for showing pictures of beads you have made.
Thanks again for the OP who started this mainly positive thread. IT is informative and cleared a lot of misconceptions.
__________________
Diana
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-06-16, 7:20am
|
|
GlassDocNC
|
|
Join Date: Aug 12, 2008
Location: Asheboro, NC
Posts: 946
|
|
Natasha at Devardi is a sweetie. I think you will be happy.
Marina
|
2009-06-18, 12:56pm
|
|
sunscreen me baby
|
|
Join Date: Jun 05, 2005
Location: Exeter, NH
Posts: 17,496
|
|
I played with my devardi for the first time today. I wasn't very impressed with the opaque salmon. I made 4 beads and finally had to resort to putting a rod in the kiln to finish the set. I'm not a fan of glass that keeps popping off the rod. I wasted almost a whole rod on shocking.
I did however like the transparent rose. I only made one bead with it, but it wasn't shocky.
The beads are in the kiln so I'll let you know if the color is something I can't live without
I've got more colors to try out tomorrow.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. ~ To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-06-18, 1:53pm
|
|
Senior Member
|
|
Join Date: Jun 27, 2005
Location: Yarmouth, Maine...home of the Clamfest
Posts: 7,693
|
|
@ Suzy....thinking about the last batch of opal yellow I had--it was TOTAL "frit on a stick"!
(and dying to see what you made!!!)
__________________
And if I laugh at any mortal thing, ‘Tis that I may not weep...” ~Lord Byron
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
new purple cricket @ home! minicc @ playing with fire in rockland! Sue & Nikki fighting over who gets to anneal the wonkies To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-06-18, 1:56pm
|
|
Senior Member
|
|
Join Date: Jan 07, 2007
Location: High Point, NC
Posts: 1,402
|
|
The salmon I have to preheat. It is wicked! But in beads is beautiful! That is the only color that I had to keep warm.
|
2009-06-18, 1:58pm
|
|
I fart diamonds
|
|
Join Date: Jun 14, 2005
Location: Altamonte Springs, FL
Posts: 3,893
|
|
The pinks need to be preheated, also.
__________________
-Shawnette the original "everybody get a grip" girl
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-06-18, 2:36pm
|
|
Senior Member
|
|
Join Date: May 23, 2006
Posts: 5,540
|
|
Me too with the opal yellow. I love the "frit on a stick" description. That's exactly what it is.
The Devardi is shocky but once heated, it's fine for me. No problem.
Quote:
Originally Posted by lunamoonshadow
@ Suzy....thinking about the last batch of opal yellow I had--it was TOTAL "frit on a stick"!
(and dying to see what you made!!!)
|
__________________
Cynthia
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-06-18, 3:51pm
|
Senior Member
|
|
Join Date: Feb 06, 2009
Posts: 501
|
|
LOL...but frit on a stick for $6/lb is better than opal yellow's current price
|
2009-06-18, 3:53pm
|
|
sunscreen me baby
|
|
Join Date: Jun 05, 2005
Location: Exeter, NH
Posts: 17,496
|
|
I do like the color. I just made simple flower discs. So I'm not going to have to worry when I try butterscotch and the opaque peach tomorrow am I?
I must be lucky. I have a great batch of opal yellow that doesn't shock. But I have a bundle of honey crunch I keep nice and dusty so I don't use it. Holding on for that hard to find resale value in 10 years, lol.
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. ~ To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-06-18, 7:02pm
|
|
Senior Member
|
|
Join Date: Jun 27, 2005
Location: Yarmouth, Maine...home of the Clamfest
Posts: 7,693
|
|
oooh, I love honey crunch--it IS aptly named though--they got the "crunch" right--it's shocky, shocky, shocky, but the color is worth it!
The devardi, if you don't pre-heat it (I don't) does best if you treat it as "shocky" (some is, some isn't) & do the "bounce, bounce, bounce" thing in the flame first, & then expect it might shock off the rod a bit...if you melt it "further out" it's easier to control & keep it so when it does crack, you can keep it melting the rod on if you're doing a bigger bead, or just spin the piece on & break it off the rod if you're about where you want to be when it happens.
I pretty much treat all glass to the bounce-bounce-bounce anyway, it's a habit I haven't lost yet from when I was hotheading out in the driveway
~luna
__________________
And if I laugh at any mortal thing, ‘Tis that I may not weep...” ~Lord Byron
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
new purple cricket @ home! minicc @ playing with fire in rockland! Sue & Nikki fighting over who gets to anneal the wonkies To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-06-18, 7:04pm
|
|
sunscreen me baby
|
|
Join Date: Jun 05, 2005
Location: Exeter, NH
Posts: 17,496
|
|
I was afraid of that. I like glass I can abuse
__________________
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. ~ To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-06-18, 7:11pm
|
|
Senior Member
|
|
Join Date: Jun 27, 2005
Location: Yarmouth, Maine...home of the Clamfest
Posts: 7,693
|
|
Try "preheating" it the way Tink does with shocky glass--the "pure propane", reduction flame, let it get coated with soot, then clean it off with a nice & blast away method then...I've used that & had great results with other shocky glasses ever since I've been going down to Rockland--I think it's one of the BEST tips Tink ever shared here--useful for every/any type of soft glass, anyone from the first time they use a oxy/propane torch can use that tip, I'm so glad she shared it!
As far as abuse--the glass is quite abuse worthy once you get it on the mandrel! It's stood up to everything I've thrown at it & I'm not real nice to my glass....'cause I'm still nowhere *near* practiced with what I'm doin'
__________________
And if I laugh at any mortal thing, ‘Tis that I may not weep...” ~Lord Byron
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts. To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
new purple cricket @ home! minicc @ playing with fire in rockland! Sue & Nikki fighting over who gets to anneal the wonkies To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
2009-06-18, 7:34pm
|
|
product of the universe
|
|
Join Date: Sep 06, 2005
Location: Rutvegas Vt
Posts: 598
|
|
here is a video of me working some devardi pink and white. Just some various action shots http://vids.myspace.com/index.cfm?fu...deoid=59220340
__________________
Chris
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
And the men who hold high places,Must be the ones to start,To mold a new reality,Closer to the heart--Rush
Currently using fire.
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -7. The time now is 11:19pm.
|