I was surprised to find you think silver tubing is softer than copper ... it's really the other way around usually (although fine silver is very soft).
However if the wall thickness is thinner (quite possible) it would be more prone to bending in the middle and might therefore seem softer to you?
I don't have the Jim Moore press but do have two other varieties plus the regular hand dapping version so you might find if you post in the silver forum/thread you might get more answers and thoughts on this.
Sadie