I keep getting broken beads. I take them out of the kiln and when I put them in water to start loosening them from the mandrel, they break in half.
|
![Old](lwe/statusicon/post_old.gif)
2019-01-10, 3:07pm
|
![Eileen's Avatar](image.php?s=6c7b0f1e50742f0e340ea2fd466d6038&u=18436&dateline=1453941718) |
Loving learning
|
|
Join Date: Oct 11, 2010
Location: Florida
Posts: 11,654
|
|
If they are breaking along the mandrel, it sounds as if they are too cool at some point. Are you going from flame to kiln? You may be admiring them too long, or just letting them cool too long before putting in the kiln.
__________________
My current "hot" fantasy involves a senior discount on glass & tools!
|
![Old](lwe/statusicon/post_old.gif)
2019-01-10, 5:20pm
|
![Three Muses Glass's Avatar](image.php?s=6c7b0f1e50742f0e340ea2fd466d6038&u=439&dateline=1313513651) |
Senior Member
|
|
Join Date: Jun 23, 2005
Location: Up and down I-95
Posts: 4,390
|
|
Hi Lory, welcome! Need lots more info- glass used, annealing schedule, did they go right in or are you batch annealing...things like that.
__________________
Rebecca
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
![Old](lwe/statusicon/post_old.gif)
2019-01-10, 6:56pm
|
![KJohn's Avatar](image.php?s=6c7b0f1e50742f0e340ea2fd466d6038&u=14203&dateline=1449370601) |
Slogan Challenged...
|
|
Join Date: Mar 21, 2009
Location: Maricopa, Arizona
Posts: 6,287
|
|
breaking in half is thermal, so sorry! that sounds very disappointing. Make sure that they have all over heat before putting into kiln, and they are not too near the door. More info would be great. HTH
__________________
Kristin ~
Facebook: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Etsy: To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
|
![Old](lwe/statusicon/post_old.gif)
2019-01-11, 7:00pm
|
![Speedslug's Avatar](image.php?s=6c7b0f1e50742f0e340ea2fd466d6038&u=19672&dateline=1586565582) |
Phill
|
|
Join Date: Mar 21, 2009
Location: Winnebago, MN
Posts: 2,489
|
|
Perhaps they are too small to hold the heat they need between the torch and the kiln.
I tended to forget that the mandrel will suck the heat out of the center of the bead and unless I was religious about putting the bead in the flame at the end for what a lot of instructors called "insurance heat".
When they are real small even 5 seconds between flame and kiln can be enough to install stress that won't show up until you begin to clean them.
Another source of stress is that your kiln is not warm enough or you are not letting the bead soak long enough in the annealing temp range for the internal stress to even out.
Cooling them too fast is yet another way to get these kinds of breaks so double check you cool down schedule of your kiln.
__________________
The Zombie Apocalypse is Upon Us.
|
Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -7. The time now is 1:22am.
|