Jelveh Designs - Glass Beads Torched One-by-One

Caber Light


 

Go Back   Lampwork Etc. > Library > Tips, Techniques, and Questions

Tips, Techniques, and Questions -- Technical questions or tips

Reply
 
Thread Tools
  #1  
Old 2013-04-04, 7:56pm
kirchybaby kirchybaby is offline
Junior Member
 
Join Date: Jan 21, 2010
Posts: 14
Default Paragon SC series question

Hello everyone,
I'm on the fence about getting a Paragon SC3. The SC series have the elements embedded in a fiber refractory casting. I have never had a fiber kiln before, but these SC series kilns look really great (on my computer screen anyway). I'm wondering if anyone has any experiences, (positive or negative) about the SC series, or smaller cast fiber kilns in general.

Here is a link to the SC-2, scroll down the page to see the embedded elements glowing through the fiber casting.

http://www.paragonweb.com/SC2_with_Window.cfm

I'm also curious if anyone feels that the skin temperatures are hotter on fiber kilns... I've noticed paragon's fiber kilns have a "second skin" to reduce skin temperature, which the refractory brick models lack. Is this an effort to circumvent a more rapid heat transmission found in fiber models?

I appreciate any and all input on the matter! Thanks very much!
Reply With Quote
  #2  
Old 2013-04-04, 9:01pm
AmorphousDesigns's Avatar
AmorphousDesigns AmorphousDesigns is offline
Wonder-wench
 
Join Date: Aug 09, 2010
Location: land of milk & honey
Posts: 1,104
Default

I have an SC2. Love it. Had to replace the relay once but it was a cheap part and easy to replace. The skin doesn't seem hot to me.
__________________
Elizabeth

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Reply With Quote
  #3  
Old 2013-04-04, 9:36pm
GabiLoraine's Avatar
GabiLoraine GabiLoraine is offline
Pincel de Fuego
 
Join Date: May 18, 2010
Location: Panama city, Panama
Posts: 406
Default

I have one and I love it. I bought the one with the simple door because it was the only one available locally and then got the bead door separately and just screwed it in, no problem. I love it. It's a great little kiln.
__________________
Gabi
Pincel de Fuego

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
/
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
/
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Reply With Quote
  #4  
Old 2013-04-04, 10:32pm
fionac fionac is offline
Senior Member
 
Join Date: Apr 07, 2012
Location: Oz
Posts: 195
Default

I've got the SC3, love it, easy to program. I have mine set for enamelling, metal clay, batch anneal and garage
Reply With Quote
  #5  
Old 2013-04-05, 9:00am
mewkittie's Avatar
mewkittie mewkittie is offline
Uh Oh....
 
Join Date: Dec 06, 2005
Posts: 1,039
Default

I have an SC2. Been using it for 9 years. Use it for annealing beads, fusing, metal clay and enameling copper. I don't know anything different as I haven't used any other type of kiln. My Glass Hive one is still sitting in it's box.
__________________
Susan

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Reply With Quote
  #6  
Old 2013-04-08, 10:48am
BeadBlossoms's Avatar
BeadBlossoms BeadBlossoms is offline
Queen Bee
 
Join Date: Oct 26, 2008
Location: Ellington, CT
Posts: 1,253
Default

I have an SC2 as well - awesome kiln! I just love it, especially it's compact size. But you can load it up with a ton of beads, etc. Go for it
__________________

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Donna


To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Vintage & Contemporary Beads, Findings, Chains, Trinity Brass, Vintaj, Bead Tubing, Bobbins



To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Handmade Artist Lampwork Jewelry
Reply With Quote
  #7  
Old 2013-04-08, 11:11am
Emily's Avatar
Emily Emily is offline
Missing presumed fed
 
Join Date: Nov 15, 2005
Location: Wherever
Posts: 3,158
Default

I have an SC -- can't remember whether it's the SC2 or SC3. I like it. I use it for metal clay and enameling as well as annealing.

However, if you make a lot of beads in one session, it might not be the best choice. You can get more mandrels in it than you might think, but it's definitely not a high-capacity kiln. If you produce a lot of beads during one session at the torch, you might consider one of the wider annealing kilns, particularly if you don't need the versatility of the SC series.

Also, if you make beads with enamel on the surface, you might want to choose a kiln with more space to keep the beads separated. The only way to get very many beads into an SC kiln is to pile them up. That's fine for most beads (after they've been in the kiln for a while and have cooled down from torch temperature to annealing temp), but because enamel has a lower melting temperature, if you pile up beads with enamel on the surface, they'll stick to each other.

I haven't had anything go wrong with my SC kiln, so I can't speak to the ease/difficulty of repairs. From what I've heard, the controller module is really easy to remove and reinstall if it needs repairs.

The outside gets warm but not what I'd call hot. As a matter of fact, a friend and I were doing some enameling on copper. Putting a wet-enameled piece on top of a kiln is a way to get the enamel to dry faster. We had a debate about whether the top of the SC kiln was warm enough for it to make any difference -- which I guess is an indication that it doesn't get very hot.

The glowing elements do look a little scary when they're that bright, but remember that the kilns are designed for metal clay, which takes much higher temperatures than we use. (If I'm remembering right, original silver PMC fired at 1760F or thereabouts.) The elements don't glow that much at annealing temp.
__________________
To those who question the real value of the Web: Sea slugs. Now, please fall into a respectful silence, and don't speak again until you understand why you were wrong.
Scorpion and one Intensity 10 lpm 20 psi concentrator

Last edited by Emily; 2013-04-08 at 11:21am.
Reply With Quote
  #8  
Old 2013-04-08, 12:58pm
Dragonharper's Avatar
Dragonharper Dragonharper is offline
Now part of the Dark Side
 
Join Date: Jul 02, 2010
Location: North Central PA
Posts: 966
Default

I have an SC3, the only draw back is the door. IT would be better for lamp working if the door opened up and not a standard swing door. If you have something in the punty door and forget and open the main door, your kiln gets swept clean.
__________________
Roy
Hot glass does not crack.
Unless it is glowing and drippy, hot glass looks like cold glass.
Reply With Quote
  #9  
Old 2013-04-08, 1:30pm
BeadBlossoms's Avatar
BeadBlossoms BeadBlossoms is offline
Queen Bee
 
Join Date: Oct 26, 2008
Location: Ellington, CT
Posts: 1,253
Default

If you are using the SC2 for beadmaking, you would order it with the bead door. You don't open the whole kiln - and the bead door can be shut for other types of firing

Oh, and I just saw them at the Glass Expo in pink and lavender!! Wish that had been an option when I bought mine way back when.
__________________

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Donna


To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Vintage & Contemporary Beads, Findings, Chains, Trinity Brass, Vintaj, Bead Tubing, Bobbins



To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Handmade Artist Lampwork Jewelry
Reply With Quote
  #10  
Old 2013-04-08, 6:56pm
GabiLoraine's Avatar
GabiLoraine GabiLoraine is offline
Pincel de Fuego
 
Join Date: May 18, 2010
Location: Panama city, Panama
Posts: 406
Default

Quote:
Originally Posted by BeadBlossoms View Post
If you are using the SC2 for beadmaking, you would order it with the bead door. You don't open the whole kiln - and the bead door can be shut for other types of firing

Oh, and I just saw them at the Glass Expo in pink and lavender!! Wish that had been an option when I bought mine way back when.
This. And me too, I saw them online in a bunch of different colors. I would have wanted it in white. I like the blue though.
__________________
Gabi
Pincel de Fuego

To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
/
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
/
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Reply With Quote
  #11  
Old 2013-04-10, 3:26pm
Kayo222's Avatar
Kayo222 Kayo222 is offline
ALWAYS SMILES
 
Join Date: Oct 13, 2011
Location: GreatLakesState
Posts: 433
Default

Yep, LOOOOVE the SC-2 with the bead door....and I pile beads on top of each other that have been enameled on a regular basis and never had one stick to another. I use a piece of kiln furniture to set my hot from the torch bead on......then when I am ready to put a new one in I remove the old one and place it on the pile (I guess by then it is cool enough?) no probs though. Only when I put a HOTTIE in there on the pile....that wasn't pretty ! And I noticed for $50 you get the hot pink, lavender or turquoise color options now!! That is awesome
__________________
MyEbay
To view links or images in signatures your post count must be 5 or greater. You currently have 0 posts.
Reply With Quote
Reply

Tags
anneal, element, fiber, holder, kiln, mandrel, paragon, refractory, skin, temperature


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 
Thread Tools

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Forum Jump




All times are GMT -7. The time now is 4:56am.


Powered by vBulletin® Version 3.7.5
Copyright ©2000 - 2024, Jelsoft Enterprises Ltd.
Your IP: 18.97.14.89